Titanium Grade 3

Contact Us

Salem Stainless Steel Suppliers Pvt. Ltd.

33 - Lawyer Chenna Thambi Street, Konditope, Kondithope, Chennai, Tamil Nadu - 600079, India

Mobile : +91-9840086688

E-mail : rajesh@ssssgroup.in


Find below the search results for the material you've specified. Please note here this information is NOT to be used for design purposes, and in no event shall MSO be liable for any damages arising from the misuse of this information. What alloys does SSSS Groups supply? Below is a comprehensive list of our alloys arranged by type. More detailed information can be found on each alloys specific page. All of our products are purchased to normal industry standards and come with material test reports (MTR) also known as material certifications. What product forms are available?
    Bar
  • Plate
  • Sheet
  • Pipe
  • Pipe Fittings
  • Flanges
  • Tube
  • Weld Wire
Find below the search results for the material you've specified. Please note here this information is NOT to be used for design purposes, and in no event shall MSO be liable for any damages arising from the misuse of this information. Titanium CP Grade 3 : Related Metals :
  • Allvac 55(tm)
  • Titan 993-Ti-grade 3(tm)
  • Timetal(r) 50A
  • RMI 55(tm)
  • Timetal(r) 50A(tm)
Specifications :
  • ASTM 4900
  • ASTM B337
  • ASTM B338
  • ASTM B381
  • ASTM F67
  • UNS R50550
Chemistry Data :
  • Carbon : 0.1 max
  • Hydrogen : 0.15 max
  • Iron : 0.3 max
  • Nitrogen : 0.05 max
  • Oxygen : 0.35 max
  • Titanium : Balance
General Information : The most corrosion resistant of all currently available titanium alloys, this grade is especially well suited to applications requiring resistance to general as well as localized crevice corrosion. Grade 7 also exhibits good strength, welding and forming Applications Generally found in chemical process and production equipment components. As a family, titanium and its alloys have developed a mystique as a nightmare to machine. This is simply not the case. Experienced operators have compared its characteristics to those found in 316 stainless steel. Recommended practice includes high coolan May be hot or cold formed using hydropress, power brake, stretch or drop hammer methods. Similar in characteristics to 300 series stainless steels. Excellent in resisting general and localized crevice corrosion in a wide range of oxidizing and reducing environments. Rated as "good" in terms of weldability. Hot forming will reduce both the springback and required forming forces, and will increase the overall ductility of the material. Rough work can be performed at 900 C (1650 F), while finishing operations should be performed at 843 C (1550 F). Hot Working Hot forming will reduce both the springback and required forming forces, and will increase the overall ductility of the material. Cold Working The cold work characteristics of this material is similar to that of a moderately tempered austenitic stainless steel. In multiple cold forming operations, intermediate stress relief is recommended to prevent tearing or other material damage. Post-work an Annealing Heat to 704 C (1300 F),hold for 2 hours follow by air cooling. For intermediate stress relieving, heat to 482-538 C(900-1000 f) and hold for 45 minutes. Other Physical Props Beta Transus (F +/- 25) 1690 Physical Data
  • Density (lb / cu. in.) : 0.163
  • Specific Heat (Btu/lb/Deg F - [32-212 Deg F]) : 0.125
  • Electrical Resistivity (microhm-cm (at 68 Deg F)) : 56
  • Melting Point (Deg F) : 3020
  • Thermal Conductivity : 9.5
  • Modulus of Elasticity Tension : 15
  • Reduction of Area : 30
Mechanical Data
  • Form : Sheet
  • Condition : Test Specimen Annealed
  • Temper : 70
Data 01
  • Form :Sheet
  • Condition : Test Specimen Annealed
  • Temper : 600
  • Tensile Strength : 32
  • Yield Strength : 20
  • Elongation : 35
  • Reduction of Area : 75
Data 02
  • Form : Sheet
  • Condition : Test Specimen Annealed
  • Temper : 800
  • Tensile Strength : 29
  • Yield Strength : 17
  • Elongation : 18
  • Reduction of Area : 75
Data 03
  • Form : Sheet
  • Condition : Test Specimen Annealed
  • Temper : 1000
  • Tensile Strength : 22
  • Yield Strength : 13
  • Elongation : 33
  • Reduction of Area : 75