Inconel 600

Contact Us

Salem Stainless Steel Suppliers Pvt. Ltd.

33 - Lawyer Chenna Thambi Street, Konditope, Kondithope, Chennai, Tamil Nadu - 600079, India

Mobile : +91-9840086688

E-mail : rajesh@ssssgroup.in


Find below the search results for the material you've specified. Please note here this information is NOT to be used for design purposes, and in no event shall MSO be liable for any damages arising from the misuse of this information. What alloys does SSSS Groups supply? Below is a comprehensive list of our alloys arranged by type. More detailed information can be found on each alloys specific page. All of our products are purchased to normal industry standards and come with material test reports (MTR) also known as material certifications. What product forms are available?
  • Bar
  • Plate
  • Sheet
  • Pipe
  • Pipe Fittings
  • Flanges
  • Tube
  • Weld Wire
Super Alloy Inconel(r) Alloy 600 Related Metals :
  • VLX600(tm)
  • AL 600(tm)
  • Ferrochronin 600(tm)
  • Nickelvac 600(tm)
  • Nicrofer 7216 LC(tm)
  • Pyromet Alloy 600(tm)
  • Sanicro 70(tm)
  • CM 600(tm)
  • Pyromet 600(tm)
Specifications :
  • AMS 5540
  • AMS 5580
  • AMS 5665
  • AMS 5687
  • ASTM B163
  • ASTM B166
  • ASTM B167
  • ASTM B168
  • ASTM B516
  • ASTM B517
  • ASTM B564
  • DIN 2.4816
  • MIL N-23228
  • MIL N-23229
  • MIL N-6710
  • MIL T-23227
  • QQ W390
  • UNS N06600
Chemistry Data :
    li>Carbon - 0.15 max
  • Chromium - 14 - 17
  • Copper - 0.5 max
  • Iron - 6 - 10
  • Manganese - 1 max
  • Nickel - Balance
  • Silicon - 0.5 max
  • Sulphur - 0.015 max
General Information Principal Design Features A general purpose structural engineering material for use at high temperatures where strength, stability, and durability are important. The alloy also has very good corrosion resistance. When considering this alloy, also investigate Alloy 690, which doub Applications Heaters, heat exchangers, chemical process equipment, heat treat furnace components and fixtures and gas turbine components. Machinability Conventional machining techniques used for iron based alloys may be used. This alloy does work-harden during machining and has higher strength and "gumminess" not typical of steels. Heavy duty machining equipment and tooling should be used to minimize c Forming This alloy has good ductility and may be readily formed by all conventional methods. Because the alloy is stronger than regular steel it requires more powerful equipment to accomplish forming. Heavy-duty lubricants should be used during cold forming. I Corrosion Resistance General corrosion resistance is good in many acid solutions, both oxidizing and reducing acids, as well as being resistant to salts. It is basically completely resistant to corrosion by organic acids. Because of the high nickel content the alloy is virt Welding The commonly used welding methods work well with this alloy. Matching alloy filler metal should be used. If matching alloy is not available then the nearest alloy richer in the essential chemistry (Ni, Co, Cr, Mo) should be used. All weld beads should Heat Treatment Solution anneal at 1850 F for 15 minutes at temperature and air cool. Forging Forging may be done in the temperature range of 2250 F to 1900 F. Hot Working The hot work temperature range is 2250 F to 1600 F. The alloy has low ductility in the range of 1200 F to 1600 F and working in that temperature range should be avoided. Cold Working Cold forming may be done using standard tooling although plain carbon tool steels are not recommended for forming as they tend to produce galling. Soft die materials (bronze, zinc alloys, etc.) minimize galling and produce good finishes, but die life is Physical Data
  • Density (lb / cu. in.) - 0.306
  • Specific Gravity - 8.47
  • Specific Heat (Btu/lb/Deg F - [32-212 Deg F]) - 0.106
  • Electrical Resistivity (microhm-cm (at 68 Deg F)) - 620
  • Melting Point (Deg F) - 2550
  • Thermal Conductivity - 103
  • Mean Coeff Thermal Expansion - 5.8
  • Magnetic Permeability - 1.01
  • Modulus of Elasticity Tension - 31.1
  • Reduction of Area - 60
Mechanical Data MSO currently has no data available for this grade.